This specification covers straight seam and spiral butt seam welded unannealed austenitic stainless steel tubular products intended for low and moderate temperatures and corrosive service where treatment is not necessary for corrosion resistance.
Standard:ASTM, ASME, DIN, EN, ISO,JIS, GOST, etc.
Steel Grades:304, 304L, 310/S, 310H, 316, 316L, 321, 321H
Product introduction
Technical data
Related Products
Service
Related Projects
Inquiry
Product introduction
Keywords(pipe type):(1)Stainless Steel Pipe, Stainless Steel Tube, Stainless Steel Tubing
Size:(2)Outside Diameter: 1/8''~24''; Wall Thickness: SCH 5 ~ Double Extra Heavy
Standard:ASTM A213, ASTM A269, ASTM A312, ASTM A358, ASTM 813
Steel Grades:304, 304L, 310/S, 310H, 316, 316L, 321, 321H
Delivery:Within 30 days and Depends on your order quantity.
Payment:TT, LC , OA , D/P
Surface:Annealed, Pickling, Polished
Packing:Bundle or bulk , seaworthy packing or for the client's requirement
Usage:In Chemical Industry, Coal, Oil Field Open Machine, Building Materials Heat-resistant Parts.
Description
Hardness :

Stainless steel tubes are commonly used to measure the hardness of Brinell, Rockwell and Vickers. Brinell hardness Among the stainless steel pipe standards, Brinell hardness is the most widely used, and the hardness of the material is often expressed by the indentation diameter, which is both intuitive and convenient. However, it is not suitable for steel pipes of harder or thinner steel.

Rockwell hardness:
The stainless steel tube Rockwell hardness test is the same as the Brinell hardness test. The difference is that it measures the depth of the indentation. The Rockwell hardness test is a widely used method in which HRC is used second only to Brinell hardness HB in steel pipe standards. Rockwell hardness can be applied to the determination of metal materials from extremely soft to very hard. It compensates for the Brinell method. It is simpler than the Brinell method and can directly read the hardness value from the dial of the hardness machine. However, due to its small indentation, the hardness value is not as accurate as the Brinell method.

Vickers hardness
The stainless steel tube Vickers hardness test is also an indentation test method for measuring very thin metal materials and surface layer hardness. It has the main advantages of Brinell and Rockwell methods, and overcomes their basic shortcomings, but it is not as simple as the Rockwell method. The Vickers method is rarely used in steel pipe standards.

Hardness test
The stainless steel tube has an inner diameter of 6.0mm or more and an annealed stainless steel tube with a wall thickness of 13mm or less. It can be a W-B75 type Vickers hardness tester. It is very fast and simple to test and is suitable for rapid and non-destructive inspection of stainless steel pipes. Stainless steel tubes with an inner diameter of more than 30 mm and a wall thickness greater than 1.2 mm are tested with a Rockwell hardness tester to test HRB and HRC hardness. Stainless steel tubes with an inner diameter of more than 30 mm and a wall thickness of less than 1.2 mm are tested with a surface Rockwell hardness tester to test HRT or HRN hardness. For stainless steel pipes with an inner diameter of less than 0 mm and greater than 4.8 mm, the hardness of HR15T is tested by a special Rockwell hardness tester for pipes. When the inner diameter of the stainless steel tube is larger than 26 mm, the hardness of the inner wall of the tube can also be tested by a Ro
Technical data
Chemical Composition
Grades C max Mn max P max S max Si max Cr Ni Mo
304 0.08 2.00 0.04 0.03 0.075 18.00-20.00 8.00-11.00 /
304L 0.035 2.00 0.04 0.03 0.075 18.00-20.00 8.00-13.00 /
316 0.08 2.00 0.04 0.03 0.075 16.00-18.00 11.00-14.00 2.00-3.00
316L 0.035 2.00 0.04 0.03 0.075 16.00-18.00 10.00-15.00 2.00-3.00

Mechanical Properties
Grades Itemper Tensile Psi Yield Psi Elong % Rockwell Hardness
304 Annealed 85000-105000 35000-75000 20-55 80-95
304L Annealed
I1/8 Hard
80000-105000 30000-75000 20-55 75-95
316 Annealed 85000 min 35000 min 50 min 80 min
  Annealed 80000 min 30000 min 50 min 75 min
Standard
Sizes of Stainless Steel Pipe

Painting & Coating
Annealed & pickled, bright annealing, polished












Related Products
Service
Certification and testing as per clients need
Third party inspections and approval
Inventory management as per clients
Logistics arrangement for client to help in cost cutting
Related Projects
Mining
2022-08-02 10:40:27
Mining
Marine engineering
2022-08-02 10:36:43
Marine engineering
Energy
2022-08-02 10:10:30
Energy
Inquiry
Copyright © GNEE(TIANJIN)MULTINATIONAL TRADE CO.,LTD All Rights Reserved.
Support: Coverweb