Alloy Pipe, Alloy Tube, Alloy Steel Pipe, Alloy Steel Tube, High Pressure Steel Pipe, Boiler Steel Pipe, ASME SA335, P11, ASTM A213
Ends :Plain End, Beveled End, Thread End
Delivery:Within 30 days and Depends on your order quantity
Product Introduction
Technical data
Related Products
Service
Related Projects
Inquiry
Product Introduction
Keywords(pipe type):Alloy Pipe, Alloy Tube, Alloy Steel Pipe, Alloy Steel Tube, High Pressure Steel Pipe, Boiler Steel Pipe, ASME SA335, P11, ASTM A213
Size:Wall thickness:1mm~120mm;Outside diameter:6mm~2500mm;Length:5.8m, 6m, 11.8m, 12m, or as required
Standard & Grade:ASTM A213, JIS G3462, JIS G3458, DIN17175, GB9948, GB 6479, etc.
ends :Plain End, Beveled End, Thread End
Delivery:Within 30 days and Depends on your order quantity
Payment:TT, LC , OA , D/P
Packing:Bundled with Hemp Rope/In Bulk
usage:Petroleum, Chemical Engineering, Electricity, Boiler
Description
Item ASTM A213 T12 Alloy steel pipe/tube
Standard ASTM A213, JIS G3462, JIS G3458, DIN17175, GB9948,GB 6479, etc.
Material T12, STBA22, 15CrMo.
Specifications Wall thickness 1mm~120mm
Outside diameter 6mm~2500mm
Length 5.8m, 6m, 11.8m, 12m, or as required.
Surface Black painted, PE coated.
Chemical composition C:0.05~0.15, Si ≤ 0.5, Mn:0.30~0.61, P≤0.025, S≤0.025, Mo:0.44~0.65, Cr:0.80-1.25
Price Term Ex-work, FOB, CIF, CFR, etc.
Payment Term TT, LC , OA , D/P
Export to Singapore, Canada, Indonesia, Korea, USA, UK, Thailand, Peru, Saudi Arabia, Viet Nam, Iran, India, Ukraine, Brazil, South Africa, etc.
Delivery Time Delivery Time: Within 30 days and Depends on your order quantity.
Package Export standard package; bundled wooden box, suit for all kinds of transport, or be required
Application 1) boiler, heat exchanger;2) Petroleum;3) Aerospace;4) chemical;5) electric power;6) Military.
Technical data
ASTM A213 Alloy Steel Chemical Composition(%, max)
Steel Grade Chemical Composition%
C Si Mn P, S Max Cr Mo Ni Max V Al Max W B Nb N
T2 0.10~0.20 0.10~0.30 0.30~0.61 0.025 0.50~0.81 0.44~0.65
T11 0.05~0.15 0.50~1.00 0.30~0.60 0.025 1.00~1.50 0.44~0.65
T12 0.05~0.15 Max 0.5 0.30~0.61 0.025 0.80~1.25 0.44~0.65
T22 0.05~0.15 Max 0.5 0.30~0.60 0.025 1.90~2.60 0.87~1.13
T91 0.07~0.14 0.20~0.50 0.30~0.60 0.02 8.0~9.5 0.85~1.05 0.4 0.18~0.25 0.015 0.06~0.10 0.03~0.07
T92 0.07~0.13 Max 0.5 0.30~0.60 0.02 8.5~9.5 0.30~0.60 0.4 0.15~0.25 0.015 1.50~2.00 0.001~0.006 0.04~0.09 0.03~0.07

ASTM A213 Alloy Steel Mechanical properties:
Steel Grade Mechanical Properties
T. S Y. P Elongation Hardness
T2 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T11 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T12 ≥ 415MPa ≥ 220MPa ≥ 30% 163HBW(85HRB)
T22 ≥ 415MPa ≥ 205MPa ≥ 30% 163HBW(85HRB)
T91 ≥ 585MPa ≥ 415MPa ≥ 20% 250HBW(25HRB)
T92 ≥ 620MPa ≥ 440MPa ≥ 20% 250HBW(25HRB)

ASTM A213 Steel Tubes Outside Diameter and Wall Thickness Tolerance
OD, mm OD Tolerance
< 25.4 +/- 0.10
25.4 – <= 38.1 +/- 0.15
> 38.1 -< 50.8 +/- 0.20
50.8 -< 63.5 +/- 0.25
63.5 -< 76.2 +/- 0.30
76.2 – <= 101.6 +/- 0.38
> 101.6 – <= 190.5 +0.38/-0.64
> 190.5 – <= 228.6 +0.38/-1.14
 
OD, mm WT Tolerance
<= 38.1 +20%/-0
> 38.1 +22%/-0
Standard
ASTM A213 Standard Scope
1.1 This specification covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes, designated Grades T91, TP304, etc. These steels are listed in Tables 1 and 2.
1.2 Grades containing the letter, H, in their designation, have requirements different from those of similar grades not containing the letter, H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements.
1.3 The tubing sizes and thicknesses usually furnished to this specification are 1/8 in. [3.2 mm] in inside diameter to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4 to 12.7 mm], inclusive, in minimum wall thickness or, if specified in the order, average wall thickness. Tubing having other diameters may be furnished, provided such tubes comply with all other requirements of this specification.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelA Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.

B It is permissible to order T2 and T12 with a sulfur content of 0.045 max. 
C Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report
 










Related Products
Service
Certification and testing as per clients need
Third party inspections and approval
Inventory management as per clients
Logistics arrangement for client to help in cost cutting
Related Projects
Oil and gas
2022-08-02 11:03:25
Oil and gas
Mining
2022-08-02 10:56:23
Mining
Marine engineering
2022-08-02 10:36:43
Marine engineering
Inquiry
Copyright © GNEE(TIANJIN)MULTINATIONAL TRADE CO.,LTD All Rights Reserved.
Support: Coverweb